| 持续荷载下混凝土的硫酸盐腐蚀研究 |
| |
| 引用本文： | 金祖权,孙伟,蒋金洋,赵铁军.持续荷载下混凝土的硫酸盐腐蚀研究[J].东南大学学报,2008,24(1):69-73. |
| |
| 作者姓名： | 金祖权 孙伟 蒋金洋 赵铁军 |
| |
| 作者单位： | 东南大学材料科学与工程学院，青岛理工大学土木工程学院 青岛266033，东南大学材料科学与工程学院，东南大学材料科学与工程学院，青岛理工大学土木工程学院，南京211189，南京211189，南京211189，青岛266033 |
| |
| 基金项目： | 国家高技术研究发展计划(863计划)，国家自然科学基金 |
| |
| 摘 要： | 研究了普通混凝土和高强混凝土在2．5％，5．0％和10％Na2SO4溶液（质量分数），以及承受不同应力比（0.25％和50％）弯曲荷载作用下的损伤失效规律、特点．结果表明：混凝土在硫酸盐溶液中腐蚀，其损伤劣化包括初始劣化段、性能改善段和性能劣化段．腐蚀溶液中Na2SO4浓度从2．5％增加到5．0％，混凝土失效时间缩短了25％左右；Na2SO4浓度增加到10％，失效时间缩短了40％．弯曲荷载在腐蚀后期加速混凝土的损伤劣化速度，应力比由0增加到25％，混凝土破坏时间降低15％；应力比增加到50％，其破坏时间降低25％～35％．此外，用SEM、能谱和XRD分析了混凝土在硫酸盐腐蚀作用下的腐蚀产物．
|
| 关 键 词： | 混凝土 硫酸盐 弯曲荷载 微观结构 |
| 修稿时间： | 2007年5月29日 |
Damage of concrete attacked by sulfate and sustained loading |
| |
| Jin Zuquan,Sun Wei,Jiang Jinyang,Zhao Tiejun.Damage of concrete attacked by sulfate and sustained loading[J].Journal of Southeast University(English Edition),2008,24(1):69-73. |
| |
| Authors: | Jin Zuquan Sun Wei Jiang Jinyang Zhao Tiejun |
| |
| Institution: | Jin Zuquan, Sun Wei, Jiang Jinyang,Zhao Tiejun (1. School of Materials Science and Engineering, Southeast University, Nanjing 211189, China;2 School of Civil Engineering, Qingdao Technological University, Qingdao 266033, China) |
| |
| Abstract: | The damage processes of ordinary concrete and high strength concrete,attacked by solutions of 2.5%,5.0% and 10%Na2SO4(mass fraction)are studied.And the effects of flexural loads with stress ratios of 25% and 50% of the initial flexural strength on the damage process of concrete are also investigated.The results show that the damage process of concrete attacked by sulfate salt exhibits an initial damaged stage,a performance improving stage and a performance worsening stage.When the concentration of Na2SO4 in a solution increases from 2.5% to 5.0%,the service time of the concrete decreases approximately 25%.Furthermore,it decreases to even 40% with an increase in a Na2SO4 concentration up to 10%.And the flexural load accelerates the deterioration rate of the concrete in the latter period.The stress ratio increases from 0 to 25%,the failure time of the concrete decreases 15%;and the failure time decreases between 25% and 35% when the stress ratio increases from 25% to 50%.In addition,sulfate corrosion products of concrete are studied by SEM (scanning electron microscopy),EDS (energy disperse spectroscopy) and XRD(X-ray diffraction). |
| |
| Keywords: | concrete sulfate flexural load microstructure |
| 本文献已被 CNKI 维普 万方数据 等数据库收录！ |
|