Structure and Dielectric Properties of Sb2O5-Doped ZrO2-SnO2-TiO2 Microwave Ceramics 总被引：1，自引：0，他引：1
The microwave frequency band is generally con-sidered in the range of 0.3—3 000 GHz. Its impor-tance is recognizable in the current growth of micro-wave communications systems which make use of thesuperior information density. Many kinds of dielectricmaterials have been developed for microwave applica-tions[1,2]. Among them, solid solution ZrO2-SnO2-TiO2(ZST) has a higher dielectric constant, a highquality factor (Q) value and a lowtemperature coeffi-cient of resonant frequency (TCF). B… 相似文献
2.
稀土钐改性TiO2光催化性能有很大的争议，基于此采用溶胶-凝胶法制备了不同掺杂量和不同温度下煅烧的光催化剂，通过XRD和亚甲基蓝的降解实验，探讨了煅烧温度、空气流速、催化剂用量和掺杂量对亚甲基蓝的降解效果。结果表明：当煅烧温度为500℃，掺杂Sm^3＋为1．2％，空气流速达到1．3L／min，催化剂用量为1．5g／L时，催化性能达到最好。 相似文献
3.
介绍了以熔盐法制备珠光颜料用片状氧化铁的最佳制备条件的探讨过程,通过在不同条件如熔盐种类、熔盐用量、煅烧温度和煅烧时间下进行合成,并使用光学显微镜对产品形貌和尺寸进行观察,从而推断出助熔剂法合成片状氧化铁的最佳条件.通过研究发现,在采用Na2SO4＋K2SO4作为复合熔盐,并且熔盐用量与三氯化铁的摩尔比为5的条件下制备前驱体,在1 100℃下煅烧4 h,可得到平均粒径约为20μm,表面平整,形貌良好的六角形片状氧化铁晶体.并对制备的片状氧化铁进行了包覆二氧化钛应用尝试,表明该法制备的片状氧化铁满足珠光颜料的要求. 相似文献
4.
以卤片和尿素为原料,采用水热合成法制备了高纯度轻质氧化镁,并对工艺条件的影响因素进行分析.结果表明,当卤片与尿素的配比为1∶4.5、反应时间为5 h、反应温度为125℃、洗涤水温度为95℃的条件下制备的氧化镁,转化率高、产品质量好,可达到分析纯轻质氧化镁的标准. 相似文献
5.
王爽 《天津职业技术师范学院学报》2010,(1):12-14,68
对稀土氧化物CeO2掺杂的BaTiO3系统微观结构和介电性能进行了研究。结果表明,在BaTiO3陶瓷中掺杂CeO2会产生细晶效应、介电常数增大以及介电损耗减小等现象。由X射线衍射仪（XRD）计算可知,c轴变长,a轴变短,增强,Ti^4＋“自发极化强度,因而介电常数有所提高。由于Ce^4＋离子进行A位取代,Ce^4＋离子半径（0．103nm）小于Ba^2＋离子半径（0．135nm）,导致晶格常数有所减小,居里温度向低温移动。掺杂CeO2的摩尔分数为0．5％的BaTiO3陶瓷在1240℃下烧成的主要性能指标为：室温介电常数ε25℃≈3160,介电损耗-0．9％,-55℃到125℃范围内最大电容量变化率不超过±15％。 相似文献
6.
以胶原纤维为模板合成了介孔TiO2-Al2O3二元复合氧化物纤维,并利用扫描电镜(SEM)、X射线衍射仪(XRD)、比表面孔隙分析仪、X光电子能谱(XPS)对该二元复合氧化物纤维进行了表征。结果表明所合成的介孔TiO2-Al2O3二元复合氧化物呈纤维状,较好地保留了胶原纤维的结构。当Ti/Al摩尔比为4.88:1时,TiO2-Al2O3二元复合氧化物纤维的平均孔径为7.4 nm,比表面积可达131.0 cm2/g,其中TiO2主要以锐钛矿相存在,Al2O3则以无定形态分散于TiO2晶体间。 相似文献
7.
研究了以稀土复合固体超强酸SO42-/TiO2/Ce4+为催化剂合成乙酸环己酯的反应,在反应温度分别为100℃、110℃、120℃下,测出酯化反应的动力学参数,建立了动力学方程,并与无催化剂作用下合成乙酸环己酯反应的活化能及动力学方程进行了比较.实验结果表明,该催化酯化反应的优化合成条件是:乙酸用量为0.262 1mol时,醇酸摩尔比为1.5:1,催化剂用量为1.0g,带水剂环己烷的加入量为12mL.稀土复合固体超强酸SO42-/TiO2/Ce4+可使反应的活化能明显降低,是合成乙酸环己酯的有效催化剂. 相似文献
8.
通过溶胶-凝胶法制备了稀土金属离子Y^3＋掺杂的TiO2光催化剂,用XRD进行了分析和表征.以紫外灯为光源,通过对结晶紫的降解反应,研究了掺杂稀土离子钇的TiO2催化活性.结果表明,Y^3＋的掺杂减小了TiO2的粒径,提高了TiO2的光催化活性,反应体系在Y^3＋掺杂量为1.2%,催化剂用量1.5g/L,经500℃煅烧的条件下制备的Y^3＋-TiO2催化下效果最好.降解浓度4.0mg/L结晶紫2小时后,降解率可达90%. 相似文献
9.
采用绿色水处理剂氧化镁处理氨氮废水,利用单因素优化分析法,对影响氧化镁处理效果的主要因素进行了研究,考察其对氧化镁处理效果的影响,确定最佳反应条件.在常温下(24℃)当氧化镁用量为2 g/L、曝气时间为2 h时氨氮去除率为99.6％,而时间再加长,用量增多,效果提升不明显.根据夏热冬冷的情况,取28℃和18℃两个温度进... 相似文献
10.
杂多酸盐催化剂催化合成丁酸乙酯 总被引：2，自引：0，他引：2
首次以杂多酸盐TiSiW1 2 O40 /TiO2 为催化剂催化合成了丁酸乙酯 .结果表明 :TiSiW1 2O40 /TiO2 具有良好的催化活性 ,乙醇和正丁酸的摩尔比为 1.5∶1,催化剂用量为反应液总量的1.0 % ,酯化反应时间为 1.5h ,反应温度为 93～ 96℃ ,丁酸乙酯的产率可达 75.6 % . 相似文献
11.
以H3 PW12 O40／TiO2－SiO2为催化剂,取代苯甲醛、乙酰乙酸乙酯和尿素为原料,无水乙醇为溶剂合成3,4－二氢嘧啶－2（1H）－酮衍生物．探讨了原料物质的量比、反应温度、催化剂用量及反应时间对收率的影响．实验表明：固定取代苯甲醛的用量为0．04 mol和无水乙醇的量为15 mL的情况下,n（取代苯甲醛）∶n（乙酰乙酸乙酯）∶n（尿素）＝1∶1．0∶1．5,催化剂的用量占反应物料总质量的1．5％,反应温度为90℃,反应时间为75 min,分别以对羟基苯甲醛、对硝基苯甲醛、茴香醛、4－氯苯甲醛、对甲氧基苯甲醛分别代替苯甲醛,产品收率为35.0％－89.2％．催化剂和合成产品分别采用IR, XRD和1 H NMR, IR, MS手段进行表征． 相似文献
12.
分别采用溶胶-凝胶法和固相反应法制备BaTiO3纳米粉体和CaCu3Ti4O12多晶块材,并系统地研究两者的介电性能。实验结果表明:BaTiO3体相陶瓷的介电性能受温度的影响较大,当频率在200~150 000 Hz范围内变动时,其室温介电常数ε最高达2 967,具有很好的频率稳定性、介电损耗小,可用来制作某些电子元件;然而CaCu3Ti4O12多晶块材的介电常数ε在(1 kHz,300 K)时高达14 000,并在100~350 K的温区内基本保持恒定,具有极好的温度稳定性。因此,在现实的应用过程中,CaCu3Ti4O12多晶块材以高介电常数、受温度影响变化小、介电损耗小等优点而更具应用前景。 相似文献
13.
YANG Shui-jin XIA Jia GAO Fei 《商丘师范学院学报》2007,23(12):81-83
Benzaldehyde 1,2 -propanediol acetal was synthesized from benzaldehyde and 1,2 -propanediol in the presence of SO42-/TiO2 - MoO3 - La2O3. The factors influencing the synthesis were discussed and the best conditions were found out. The optimum conditions are: molar ratio of benzaldehyde to 1,2 - propanediol is 1: 1.8, the quantity of catalyst is equal to 1.0% feed stock, and the reaction time is 1.0 h. SO42-/TiO2 -MoO3 -La2O3 is an excellent catalyst for synthesizing benzaldehyde 1,2 - propanediol acetal and its yield can reach over 77.2%. 相似文献
14.
Researchershavebecomeincreasinglyinterestedinironaluminideintermetallics (includingFe3AlandFeAl)since 1970sinviewofthecombinationoflowcost,lowerdensity ,remarkableresistancetoerosion ,sulfidizingandoxidizingathightemperature .However ,industrialap plicationofthesealloyshasbeenverylimitedduetotheirpoorductilityandfracturetoughnessatroomtemperatureaswellastheirdifficultyinshaping[1] .Somestudieshaveindicatedthatcoatingstructuralmaterialswithironaluminidesbyusingthermalsprayingwillnotonlysolveth… 相似文献
15.
以钛酸四丁酯和硝酸钙为原料,用改进的固相反应法成功合成了CaTiO3：Pr红色荧光粉.为了提高这种荧光粉的发光性能,加入铝离子作为电荷补偿剂,硼酸作为助熔剂,以及加入锌离子和镁离子替代一部分钙离子,并对其发光性能的影响进行了研究.采用X射线衍射、荧光分光光度计和扫描电镜研究了CaTiO3：Pr的物相组成,发光性质和颗粒形貌.结果表明一定量的硼酸、铝离子、镁离子、锌离子能够有效的提高CaTiO3：Pr红色荧光粉发光强度.余辉曲线和发光亮度表明当硼酸与硝酸钙的物质的量之比为0.3,铝离子与硝酸钙的物质的量之比为0.001时Ca0.8Zn0.2TiO3：Pr,Ca0.9Mg0.1TiO3：Pr样品具有最佳的发光性能. 相似文献
16.
MN2 DOPED ZN2SIO4 PHOSPHORS WERE SYNTHESIZED BY SOL-GEL METHOD, AND THE INFLUENCE OF ZINC SOURCE. MN2 DOPANT CONCENTRATION AND ANNEALING TEMPERATURE WERE INVESTIGATED. RESULTS SHOW THAT ZINC NITRATE BASED PRECURSOR WITH STRONG GREEN EMISSION INTENSITIES IS BETTER THAN ZINC ACETATE BASED PRECURSOR. THE INTENSITY OF GREEN LIGHT EMISSION REACHES A PEAK AT 254 NM WHEN THE MN2 DOPANT CONCENTRATION IS ABOUT 5%( MOLAR PERCENTAGE). STRUCTURAL DETAILS OF THE PHOSPHORS WERE EXAMINED THROUGH X-RAY DIFFRACTOMETRY. THERMOGRAVIMETRIC AND DIFFERENTIAL THERMAL ANALYSIS. THE RESULT INDICATES THAT THEY ARE BOTH RHOMBOHEDRAL STRUCTURES, WHICH REMAIN AMORPHOUS BELOW 700 ℃ AND CRYSTALLIZE COMPLETELY AROUND 1 000 ℃. THE LUMINESCENT PROPERTIES OF ZN:SIO4/MN2 PHOSPHORS WERE CHARACTERIZED BY EXCITATION AND EMISSION SPECTRA. 相似文献
17.
以柠檬酸和正戊醇为原料,采用自制的稀土固体超强酸SO4^2-／TiO2／La^3＋、SO4^2-／SnO2／La^3＋、SO4^2-／ZrO2／La^3＋、SO4^2-／Fe2O3／La^3＋为催化剂催化合成增塑剂柠檬酸三戊酯．通过单因素和正交实验考察了各反应因素对反应酯化率的影响．实验表明：当柠檬酸与正戊醇摩尔比为1：4．0、S04^2-／TiO2／La^3＋催化剂用量为柠檬酸总量的4％、催化荆活化温度为250℃、反应温度140-150℃和反应时间3．0h条件下,柠檬酸三戊酯的酯化率可达到97．3％,催化剂重复使用多次,活性未见明显降低．产品经红外光谱定性分析,纯度经气相色谱分析大于99％． 相似文献
18.
采用sol-gel法制备了锐钛矿型TiO2薄膜与Ni2＋掺杂TiO2薄膜。通过XRD、AFM表征了薄膜的晶相和形貌特征,用接触角测定仪测定接触角以评估薄膜的亲水性,以甲基橙作为有机污染物研究了薄膜的光催化性能。实验结果发现：少量Ni2＋掺杂提高了TiO2薄膜的亲水性和光致亲水性。但Ni2＋掺杂却使TiO2光催化性能有所降低。结果表明,TiO2薄膜表面的光致亲水性与光催化特性无正相关性。 相似文献
19.
以钛酸四丁酯为原料,在高浓度的硝酸溶液条件下,采用低温水解方法合成微晶TiO2光催化剂,分别采用XRD、FITR、SEM、TEM、PL等测试技术对催化剂进行了表征。实验结果表明:在低温85℃条件下,加入65 mL硝酸可以制得结构和形貌不同的TiO2微晶,该材料在225 nm波长诱导下表现出420 nm的发光性能。所得TiO2微晶60 min之内可在太阳光照射条件下将25 mg/L的甲基橙完全分解。 相似文献
20.
以钛酸四丁酯为原料,在高浓度的硝酸溶液条件下,采用低温水解方法合成微晶TiO2光催化剂,分别采用XRD、FTTR、SEM、TEM、PL等测试技术对催化剂进行了表征。实验结果表明：在低温85℃条件下,加入65mL硝酸可以制得结构和形貌不同的HO2微晶,该材料在225nm波长诱导下表现出420砌的发光性能。所得TiO2微晶60min之内可在太阳光照射条件下将25mg／L的甲基橙完全分解。 相似文献